PAD PRINTABLE RADIO OPAQUE INK移印X射线照影油墨

移印X射线照影油墨
描述:119-31TS是一种较其灵活的，可移印无线电不透明油墨和涂料的应用
移印和注射器点胶。该产品对PEBAX、Kapton、Mylar、玻璃等具有优良的附着力
多种其他基质。与传统材料不同，该产品具有性能平衡的特点
具有优良的韧性、高屈曲、高折痕、高耐磨性以及拉伸、拉伸的能力。
这些特性使119-31TS非常适合的应用包括，但不限于，制造标记
用于医疗设备和透视镜以及安全应用的屏蔽。119-31TS的化学成分更强
耐119-31T型。
典型的属性:
粘度(cps) 11000
百分比填料(固化
密度(固化，g/cc) 12.05
交叉粘合(PEBAX) 5B
铅笔硬度F
使用温度范围(°C) -55到+200
热稳定性(°C)良好到+250
建议处理:119-31TS可随货使用。进一步的细化可能由
加入少量CMI稀释剂113-39或127-32R2。在使用之前，一定要混合好重新悬浮填料
建议固化:较好的性能，对于大多数应用，结果固化后，以下一种固化
但是在110°C到200°C的温度范围内可以达到良好的效果。建议终端用户
通过实验确定温度和时间，在较高的温度下，较适合个别应
推荐用于不易粘附基材。

119-31TS EXTREMELY FLEXIBLE PAD PRINTABLE RADIO OPAQUE INK DESCRIPTION: 119-31TS is an extremely flexible, pad printable radio opaque ink and coating for application by pad printing and syringe dispensing. The product features excellent adhesion to PEBAX, Kapton, Mylar, glass and a variety of other substrates. Unlike conventional materials this product offers a balance of properties featuring excellent toughness high flexing, crease, and abrasion resistance as well as the ability to elongate and stretch. These properties make 119-31TS well suited for applications including, but not limited to, manufacturing of markers for medical devices and fluoroscopy as well as shielding for security applications. 119-31TS is a more chemically resistant version of 119-31T. TYPICAL PROPERTIES: Viscosity (cps) 11,000 Percent Filler (cured) > 95 Density (cured, g/cc) 12.05 Crosshatch Adhesion (PEBAX) 5B Pencil Hardness F Useful Temperature Range (°C) -55 to +200 Thermal Stability (°C) Good to +250 SUGGESTED HANDLING: 119-31TS is ready to use as supplied. Further thinning may be accomplished by adding small amounts of CMI thinners 113-39 or 127-32R2. Prior to use, be certain to mix well to resuspend filler. SUGGESTED CURING: Best properties, for most applications, result when cured following one of the below cure schedules but good results can be attained with temperatures between 110° and 200°C. End user is advised to experimentally determine temperature and time best suited for individual applications though higher temperatures are recommended for difficult to stick to substrates.